2 FABRICATION PROCESSES The mixture of reinforcement/resin does not really become a composite material until the last phase of the fabrication,that is,when the matrix is hardened.After this phase,it would be impossible to modify the material,as in the way one would like to modify the structure of a metal alloy using heat treatment,for example. In the case of polymer matrix composites,this has to be polymerized,for example, polyester resin.During the solidification process,it passes from the liquid state to the solid state by copolymerization with a monomer that is mixed with the resin The phenomenon leads to hardening.This can be done using either a chemical (accelerator)or heat.The following pages will describe the principal processes for the formation of composite parts. 2.1 MOLDING PROCESSES The flow chart in Figure 2.1 shows the steps found in all molding processes. Forming by molding processes varies depending on the nature of the part,the number of parts,and the cost.The mold material can be made of metal,polymer, wood,or plaster. 2.1.1 Contact Molding Contact molding(see Figure 2.2)is open molding (there is only one mold,either male or female).The layers of fibers impregnated with resin (and accelerator)are placed on the mold.Compaction is done using a roller to squeeze out the air pockets.The duration for resin setting varies,depending on the amount of accel- erator,from a few minutes to a few hours.One can also obtain parts of large dimensions at the rate of about 2 to 4 parts per day per mold. 2.1.2 Compression Molding With compression molding (see Figure 2.3).the countermold will close the mold after the impregnated reinforcements have been placed on the mold.The whole assembly is placed in a press that can apply a pressure of 1 to 2 bars.The polymerization takes place either at ambient temperature or higher. The process is good for average volume production:one can obtain several dozen parts a day (up to 200 with heating).This has application for automotive and aerospace parts. 2003 by CRC Press LLC
2 FABRICATION PROCESSES The mixture of reinforcement/resin does not really become a composite material until the last phase of the fabrication, that is, when the matrix is hardened. After this phase, it would be impossible to modify the material, as in the way one would like to modify the structure of a metal alloy using heat treatment, for example. In the case of polymer matrix composites, this has to be polymerized, for example, polyester resin. During the solidification process, it passes from the liquid state to the solid state by copolymerization with a monomer that is mixed with the resin. The phenomenon leads to hardening. This can be done using either a chemical (accelerator) or heat. The following pages will describe the principal processes for the formation of composite parts. 2.1 MOLDING PROCESSES The flow chart in Figure 2.1 shows the steps found in all molding processes. Forming by molding processes varies depending on the nature of the part, the number of parts, and the cost. The mold material can be made of metal, polymer, wood, or plaster. 2.1.1 Contact Molding Contact molding (see Figure 2.2) is open molding (there is only one mold, either male or female). The layers of fibers impregnated with resin (and accelerator) are placed on the mold. Compaction is done using a roller to squeeze out the air pockets. The duration for resin setting varies, depending on the amount of accelerator, from a few minutes to a few hours. One can also obtain parts of large dimensions at the rate of about 2 to 4 parts per day per mold. 2.1.2 Compression Molding With compression molding (see Figure 2.3), the countermold will close the mold after the impregnated reinforcements have been placed on the mold. The whole assembly is placed in a press that can apply a pressure of 1 to 2 bars. The polymerization takes place either at ambient temperature or higher. The process is good for average volume production: one can obtain several dozen parts a day (up to 200 with heating). This has application for automotive and aerospace parts. TX846_Frame_C02 Page 17 Monday, November 18, 2002 10:40 AM © 2003 by CRC Press LLC
Reinforcement Resin impregnation(mixing) 4↓ placing mixture on tool ↓ compaction ↓ polymerization ↓ demold ↓ finishing Figure 2.1 Steps in Molding Process Reinforcement:glass;Kevlar Roller Matrix:polyester resin Release agent gel coat Figure 2.2 Contact Molding Reinforcement Matrix counter mold Release agent+ mold gel coat Figure 2.3 Compression Molding 2003 by CRC Press LLC
Figure 2.1 Steps in Molding Process Figure 2.2 Contact Molding Figure 2.3 Compression Molding TX846_Frame_C02 Page 18 Monday, November 18, 2002 10:40 AM © 2003 by CRC Press LLC
Seal putty Soft plastic film Atmospheric pressure Felt for pumping ↓ Vacuum pump Laminate Separator Figure 2.4 Vacuum Molding Accelerator Biological protection 20 kw-10 MeV Laminate under pressure Electron beam X rays e≤300mm e≤25mm Figure 2.5 Electron Beam or X-ray Molding 2.1.3 Molding with Vacuum This process of molding with vacuum is still called depression molding or bag molding.As in the case of contact molding described previously,one uses an open mold on top of which the impregnated reinforcements are placed.In the case of sandwich materials,the cores are also used (see Chapter 4).One sheet of soft plastic is used for sealing(this is adhesively bonded to the perimeter of the mold).Vacuum is applied under the piece of plastic (see Figure 2.4).The piece is then compacted due to the action of atmospheric pressure,and the air bubbles are eliminated.Porous fabrics absorb excess resin.The whole material is polymerized by an oven or by an autoclave under pressure(7 bars in the case of carbon/epoxy to obtain better mechanical properties).or with heat,or with electron beam,or x-rays;see Figure 2.5).This process has applications for aircraft structures,with the rate of a few parts per day (2 to 4). 2003 by CRC Press LLC
2.1.3 Molding with Vacuum This process of molding with vacuum is still called depression molding or bag molding. As in the case of contact molding described previously, one uses an open mold on top of which the impregnated reinforcements are placed. In the case of sandwich materials, the cores are also used (see Chapter 4). One sheet of soft plastic is used for sealing (this is adhesively bonded to the perimeter of the mold). Vacuum is applied under the piece of plastic (see Figure 2.4). The piece is then compacted due to the action of atmospheric pressure, and the air bubbles are eliminated. Porous fabrics absorb excess resin. The whole material is polymerized by an oven or by an autoclave under pressure (7 bars in the case of carbon/epoxy to obtain better mechanical properties), or with heat, or with electron beam, or x-rays; see Figure 2.5). This process has applications for aircraft structures, with the rate of a few parts per day (2 to 4). Figure 2.4 Vacuum Molding Figure 2.5 Electron Beam or X-ray Molding TX846_Frame_C02 Page 19 Monday, November 18, 2002 10:40 AM © 2003 by CRC Press LLC
Resin Figure 2.6 Resin Injection Molding heated mold mat thermoset resin heater counter- mold Figure 2.7 Injection of Premixed Heaters Mat+Themmoplastic resin Figure 2.8 Injection of Thermoplastic Premixed 2.1.4 Resin Injection Molding With resin injection molding(see Figure 2.6).the reinforcements(mats,fabrics)are put in place between the mold and countermold.The resin (polyester or phenolic) is injected.The mold pressure is low.This process can produce up to 30 pieces per day.The investment is less costly and has application in automobile bodies. 2.1.5 Molding by Injection of Premixed The process of molding by injection of premixed allows automation of the fabrication cycle(rate of production up to 300 pieces per day). Thermoset resins:Can be used to make components of auto body.The schematic of the process is shown in Figure 2.7. Thermoplastic resins:Can be used to make mechanical components with high temperature resistance,as shown in Figure 2.8. 2003 by CRC Press LLC
2.1.4 Resin Injection Molding With resin injection molding (see Figure 2.6), the reinforcements (mats, fabrics) are put in place between the mold and countermold. The resin (polyester or phenolic) is injected. The mold pressure is low. This process can produce up to 30 pieces per day. The investment is less costly and has application in automobile bodies. 2.1.5 Molding by Injection of Premixed The process of molding by injection of premixed allows automation of the fabrication cycle (rate of production up to 300 pieces per day). Thermoset resins: Can be used to make components of auto body. The schematic of the process is shown in Figure 2.7. Thermoplastic resins: Can be used to make mechanical components with high temperature resistance, as shown in Figure 2.8. Figure 2.6 Resin Injection Molding Figure 2.7 Injection of Premixed Figure 2.8 Injection of Thermoplastic Premixed TX846_Frame_C02 Page 20 Monday, November 18, 2002 10:40 AM © 2003 by CRC Press LLC
isocyanate mold counter mold (low pressure “isocyanate+ and temperature polyol" >polyurethane mixture foam Polyol cut fibers Figure 2.9 Foam Injection Fabric reinforcement Mold Resin Heating Short fiber reinforcement Figure 2.10 Centrifugal Molding 2.1.6 Molding by Foam Injection Molding by foam injection (see Figure 2.9)allows the processing of pieces of fairly large dimensions made of polyurethane foam reinforced with glass fibers. These pieces remain stable over time,with good surface conditions.and have satisfactory mechanical and thermal properties. 2.1.7 Molding of Components of Revolution The process of centrifugal molding (see Figure 2.10)is used for the fabrication of tubes.It allows homogeneous distribution of resin with good surface conditions. including the internal surface of the tube.The length of the tube depends on the length of the mold.Rate of production varies with the diameter and length of the tubes(up to 500 kg of composite per day). The process of filament winding (see Figure 2.11)can be integrated into a continuous chain of production and can fabricate tubes of long length.The rate of production can be up to 500 kg of composite per day.These can be used to make missile tubes,torpillas,containers,or tubes for transporting petroleum. For pieces which must revolve around their midpoint,winding can be done on a mandrel.This can then be removed and cured in an autoclave (see Figure 2.12).The fiber volume fraction is high (up to 85%).This process is used to fabricate components of high internal pressure,such as reservoirs and propulsion nozzles. 2003 by CRC Press LLC
2.1.6 Molding by Foam Injection Molding by foam injection (see Figure 2.9) allows the processing of pieces of fairly large dimensions made of polyurethane foam reinforced with glass fibers. These pieces remain stable over time, with good surface conditions, and have satisfactory mechanical and thermal properties. 2.1.7 Molding of Components of Revolution The process of centrifugal molding (see Figure 2.10) is used for the fabrication of tubes. It allows homogeneous distribution of resin with good surface conditions, including the internal surface of the tube. The length of the tube depends on the length of the mold. Rate of production varies with the diameter and length of the tubes (up to 500 kg of composite per day). The process of filament winding (see Figure 2.11) can be integrated into a continuous chain of production and can fabricate tubes of long length. The rate of production can be up to 500 kg of composite per day. These can be used to make missile tubes, torpillas, containers, or tubes for transporting petroleum. For pieces which must revolve around their midpoint, winding can be done on a mandrel. This can then be removed and cured in an autoclave (see Figure 2.12). The fiber volume fraction is high (up to 85%). This process is used to fabricate components of high internal pressure, such as reservoirs and propulsion nozzles. Figure 2.9 Foam Injection Figure 2.10 Centrifugal Molding TX846_Frame_C02 Page 21 Monday, November 18, 2002 10:40 AM © 2003 by CRC Press LLC